LAP100.29 is a kind of ultra-pure water atomized iron powder. With apparent density 2.95-3.10g/cm3, good compressive performance, wide range of application, and it is widely used in the production of high strength and high density sintered structural parts....

LAP100.29H is a type of ultra-pure water atomised iron powder, with AD 2.95-3.10g/cm3, with good compression performance, and is widely used in high strength, high density sintered structural PM parts....

LAP100.29D1 Add Ni(1.70-2.10%)and Cu(1.60-1.90%)in to the base powder(LAP100.29Mo1)mix uniformly. It enables the powder has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials. ·The powder has high......

LAP100.29D2
Composition: Ni(3.8-4.20%), Cu(1.60-1.90%), Mo(0.5-0.7%)
This diffusion alloyed powder grade has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials. ·The powder has high………………………

LAP100.29Mo1: Add Mo (0.50-0.70%)into the molten steel,which enables all alloy elements fully integrated into the molten steel.The powder has high compressibility and high hardenability.This type of power is mainly used for production of good heat treatment performance parts. ·Good heat......

LAP100.29Mo2: Add Mo (0.80-1.00%)into the molten steel,which enables all alloy elements fully integrated into the molten steel.The powder has high compressibility and high hardenability.This type of power is mainly used for production of good heat treatment performance parts. ·Good heat......

LAP100.29Mo3: Add Mo (1.40-1.60%)into the molten steel,which enables all alloy elements fully integrated into the molten steel.The powder has high compressibility and high hardenability.This type of power is mainly used for production of good heat treatment performance parts. ·Good heat......

LAP100.29D3
Composition: Ni(3.80-4.20%), Cu(1.80-2.20%), Mo(1.40-1.60%)
This diffusion alloyed powder grade has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials. ·The powder has high………………………

LAP100.29D4
Composition: Ni(1.40-1.60%), Cu(1.80-2.20%), Mo(0.50-0.70%)
This diffusion alloyed powder grade has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials. ·The powder has high………………………

LAP100.29A1: Add Ni(1.70-2.00%)and Mo(0.40-0.60%)into the molten steel,which enables all alloy elements fully integrated into the molten steel The powder has high strength and good heat treatment performance This type of power is mainly used for production of forging parts and high strength......