LAP100.29Mo1: Add Mo (0.50-0.70%)into the molten steel,which enables all alloy elements fully integrated into the molten steel. The powder has high compressibility and high hardenability. This type of power is mainly used for production of good heat treatment performance parts.
Advantages：
·Good heat treatment permance,by adding Mo improves sintered parts'wear resistance and hardenability.
·Sintered parts after quenching have high strength and high performance treatment..
·The alloy elements distribute uniformly without segregation, which has uniformsintering performance.
Specification
Chemical Properties（%） | Unit | Specification | |
| Min | Max | ||
| C | % | 0.01 | |
| Si | % | 0.05 | |
| Mn | % | 0.15 | |
| P | % | 0.02 | |
| S | % | 0.015 | |
| Mo | % | 0.50 | 0.70 |
| Physical Properties | |||
| Apparent density | g/cm3 | 3.00 | 3.30 |
| Flow rate | s/50g | 30 | |
| Green density 600Mpa | g/cm3 | 7.06 | |
| Particle size distribution（%） | |||
| 180-212um | % | 1 | |
| 150-180um | % | 10 | |
| 45-150um | % | ||
| -45um | % | 10 | 30 |
Properties
LAP100.29Mo1 + 0.5%C + 0.8%Zn-st, conditions: temperature1120℃; Sintering time 30min; Sintering
density 7.0(g/m³); Rockwell hardness(HRB) 78; Tensity strength(MPa) 410; Elongation(%) 1.95;
Impact energy(J) 21.
Specifications of other Mo Alloy Powders
Product Packing
25kg/bag, 1000kg/bag, the package can be customized by buyer's requirements.
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.
LAP100.29Mo1: Add Mo (0.50-0.70%)into the molten steel,which enables all alloy elements fully integrated into the molten steel. The powder has high compressibility and high hardenability. This type of power is mainly used for production of good heat treatment performance parts.
Advantages：
·Good heat treatment permance,by adding Mo improves sintered parts'wear resistance and hardenability.
·Sintered parts after quenching have high strength and high performance treatment..
·The alloy elements distribute uniformly without segregation, which has uniformsintering performance.
Specification
Chemical Properties（%） | Unit | Specification | |
| Min | Max | ||
| C | % | 0.01 | |
| Si | % | 0.05 | |
| Mn | % | 0.15 | |
| P | % | 0.02 | |
| S | % | 0.015 | |
| Mo | % | 0.50 | 0.70 |
| Physical Properties | |||
| Apparent density | g/cm3 | 3.00 | 3.30 |
| Flow rate | s/50g | 30 | |
| Green density 600Mpa | g/cm3 | 7.06 | |
| Particle size distribution（%） | |||
| 180-212um | % | 1 | |
| 150-180um | % | 10 | |
| 45-150um | % | ||
| -45um | % | 10 | 30 |
Properties
LAP100.29Mo1 + 0.5%C + 0.8%Zn-st, conditions: temperature1120℃; Sintering time 30min; Sintering
density 7.0(g/m³); Rockwell hardness(HRB) 78; Tensity strength(MPa) 410; Elongation(%) 1.95;
Impact energy(J) 21.
Specifications of other Mo Alloy Powders
Product Packing
25kg/bag, 1000kg/bag, the package can be customized by buyer's requirements.
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.