LAP100.29H is a type of ultra-pure water atomised iron powder, with AD 2.95-3.10g/cm3, with good compression performance, and is widely used in high strength, high density sintered structural PM parts.
·High purity, easy compression, good fluidity, used for the production of high density PM structural parts.
·Fixed-volume batch mixing, maintaining the stability of different batches of powder.
·Irregular particle shape, compactibility.
·High purity, used as the iron magnetic material base.
Product standard and content(wt%) | |||||||||||||
Composition | Fe | C | S | Si | Mn | P | O | Al | Cr | Ti | V | Cu | Ni |
Standard | ≥99.5 | ≤0.01 | ≤0.012 | ≤0.04 | ≤0.12 | ≤0.012 | ≤0.12 | - | - | - | - | - | - |
Classic | 99.65 | 0.003 | 0.008 | 0.02 | 0.08 | 0.01 | 0.08 | 0.005 | 0.01 | 0.001 | 0.006 | 0.02 | 0.007 |
Sieve analysis (particle size distribution) | ||||||
μm | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
wt% | 0 | ≤10 | balance | balance | balance | 15-30 |
Classic | 0 | 2 | 20.2 | 24.7 | 31.5 | 21.6 |
Properties
Under sintering temperature of 1120℃, sintering hardness (HRB)90; Tensile strength(MPa) 485; Elongation(%)1.75; Impact powder(J)18.5; Sintering expansion rate 0.25%.
Package and delivery
1000kg per big flexbag and 25kg per small bag packed into one big bag
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.
LAP100.29H is widely used for the production of sintered metal parts with density above 6.8g/cm3 and PM forged parts.
LAP100.29H is a type of ultra-pure water atomised iron powder, with AD 2.95-3.10g/cm3, with good compression performance, and is widely used in high strength, high density sintered structural PM parts.
·High purity, easy compression, good fluidity, used for the production of high density PM structural parts.
·Fixed-volume batch mixing, maintaining the stability of different batches of powder.
·Irregular particle shape, compactibility.
·High purity, used as the iron magnetic material base.
Product standard and content(wt%) | |||||||||||||
Composition | Fe | C | S | Si | Mn | P | O | Al | Cr | Ti | V | Cu | Ni |
Standard | ≥99.5 | ≤0.01 | ≤0.012 | ≤0.04 | ≤0.12 | ≤0.012 | ≤0.12 | - | - | - | - | - | - |
Classic | 99.65 | 0.003 | 0.008 | 0.02 | 0.08 | 0.01 | 0.08 | 0.005 | 0.01 | 0.001 | 0.006 | 0.02 | 0.007 |
Sieve analysis (particle size distribution) | ||||||
μm | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
wt% | 0 | ≤10 | balance | balance | balance | 15-30 |
Classic | 0 | 2 | 20.2 | 24.7 | 31.5 | 21.6 |
Properties
Under sintering temperature of 1120℃, sintering hardness (HRB)90; Tensile strength(MPa) 485; Elongation(%)1.75; Impact powder(J)18.5; Sintering expansion rate 0.25%.
Package and delivery
1000kg per big flexbag and 25kg per small bag packed into one big bag
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.
LAP100.29H is widely used for the production of sintered metal parts with density above 6.8g/cm3 and PM forged parts.