LAP100.29D1 Add Ni(1.70-2.10%)and Cu(1.60-1.90%)in to the base powder(LAP100.29Mo1)mix uniformly. It enables the powder has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials. ·The powder has high......
LAP100.29D2 Composition: Ni(3.8-4.20%), Cu(1.60-1.90%), Mo(0.5-0.7%) This diffusion alloyed powder grade has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials. ·The powder has high………………………
LAP100.29Mo1: Add Mo (0.50-0.70%)into the molten steel,which enables all alloy elements fully integrated into the molten steel.The powder has high compressibility and high hardenability.This type of power is mainly used for production of good heat treatment performance parts. ·Good heat......
LAP100.29Mo2: Add Mo (0.80-1.00%)into the molten steel,which enables all alloy elements fully integrated into the molten steel.The powder has high compressibility and high hardenability.This type of power is mainly used for production of good heat treatment performance parts. ·Good heat......
LAP100.29Mo3: Add Mo (1.40-1.60%)into the molten steel,which enables all alloy elements fully integrated into the molten steel.The powder has high compressibility and high hardenability.This type of power is mainly used for production of good heat treatment performance parts. ·Good heat......
LAP100.29D3 Composition: Ni(3.80-4.20%), Cu(1.80-2.20%), Mo(1.40-1.60%) This diffusion alloyed powder grade has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials. ·The powder has high………………………
LAP100.29D4 Composition: Ni(1.40-1.60%), Cu(1.80-2.20%), Mo(0.50-0.70%) This diffusion alloyed powder grade has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials. ·The powder has high………………………
LAP100.29A1: Add Ni(1.70-2.00%)and Mo(0.40-0.60%)into the molten steel,which enables all alloy elements fully integrated into the molten steel The powder has high strength and good heat treatment performance This type of power is mainly used for production of forging parts and high strength......
LAP100.29A2: Add Cr, Ni, Mo, Co into the molten steel, which enables the all alloy elements fully integrated into the molten steel. The powder has high strength,good heat treatment performance and corrosion resistance. This type of power is mainly used for production of high strength sintered machine parts, wear resistant parts, corrosion resistant in bad working environment sintered parts,e.g.valve seats.