LAP100.29M01: Add Mo (0.50-0.70%)into the molten steel,which enables all alloy elements fully integrated into the molten steel. The powder has high compressibility and high hardenability. This type of power is mainly used for production of good heat treatment performance parts.
·Good heat treatment permance,by adding Mo improves sintered parts'wear resistance and hardenability.
·Sintered parts after quenching have high strength and high performance treatment..
·The alloy elements distribute uniformly without segregation, which has uniformsintering performance.
| Product standard and content(wt%) | ||||||||
| Composition | Fe | C | S | Si | M | P | 0 | Mo |
| Standard | balance | ≤0.01 | ≤0.15 | ≤0.05 | ≤0.15 | ≤0.020 | ≤0.20 | 0.50-0.70 |
| Classic | - | 0.005 | 0.01 | 0.03 | 0.12 | 0.01 | 0.1 | 0.55 |
| Sieve analysis(particle size distribution) | ||||||
| um | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
| wt% | ≤1 | ≤10 | balance | balance | balance | 15-30 |
| Classic | trace | 1 | 16.5 | 24 | 31 | 27.5 |
Package and delivery
1000kg per big flexbag and 25kg per small bag packed into one big bag.
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.
LAP100.29M01: Add Mo (0.50-0.70%)into the molten steel,which enables all alloy elements fully integrated into the molten steel. The powder has high compressibility and high hardenability. This type of power is mainly used for production of good heat treatment performance parts.
·Good heat treatment permance,by adding Mo improves sintered parts'wear resistance and hardenability.
·Sintered parts after quenching have high strength and high performance treatment..
·The alloy elements distribute uniformly without segregation, which has uniformsintering performance.
| Product standard and content(wt%) | ||||||||
| Composition | Fe | C | S | Si | M | P | 0 | Mo |
| Standard | balance | ≤0.01 | ≤0.15 | ≤0.05 | ≤0.15 | ≤0.020 | ≤0.20 | 0.50-0.70 |
| Classic | - | 0.005 | 0.01 | 0.03 | 0.12 | 0.01 | 0.1 | 0.55 |
| Sieve analysis(particle size distribution) | ||||||
| um | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
| wt% | ≤1 | ≤10 | balance | balance | balance | 15-30 |
| Classic | trace | 1 | 16.5 | 24 | 31 | 27.5 |
Package and delivery
1000kg per big flexbag and 25kg per small bag packed into one big bag.
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.