LAP100.29D1: Add Ni(1.70-2.10%)and Cu(1.60-1.90%)in to the base powder(LAP100.29Mo1)mix uniformly. It enables the powder has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials.
·The powder has high compressibility and high strength.
·By adding superfine Cu powder improves powders uniformity and stability.
·Suitable for production of high strength and high dimensional precision high quality PM parts.
| Product standard and content(wt%) | ||||||||||
| Composition | Fe | C | S | Si | Mn | P | O | Mo | Cu | Ni |
| Standard | balance | ≤0.015 | ≤0.015 | ≤0.05 | ≤0.15 | ≤0.015 | ≤0.15 | 0.5-0.7 | 1.6-1.9 | 1.7-2.1 |
| Classic | - | 0.006 | 0.008 | 0.03 | 0.1 | 0.01 | 0.11 | 0.52 | 1.72 | 1.75 |
Sieve analysis (particle size distribution) | ||||||
| um | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
| wt% | trace | ≤1 | balance | balance | balance | 10-30 |
| Classic | 0 | 0.3 | 16.5 | 25 | 30.2 | 20.8 |
Properties
LAP100.29D1+0.3%C+0.6%Zn-st, condition: temperature1120℃, sintering time 30min.
LAP100.29D2: Add Ni(3.80-4.20%)and Cu(1.60-1.90%)into the base powder(LAP100.29Mo1) mix uniformly.Due to its high Ni content, it is suitable for production of high hardcnability and high strength parts.
·The powder has high compressibility and high strength.
·No segregation enables the stability of product's sintered size.
·The increase of Ni content improves the hardenability of the material.
·Suitable for the production of large parts which need heat treatment.
| Product standard and content(wt%) | ||||||||||
| Composition | Fe | C | S | Si | Mn | P | O | Mo | Cu | Ni |
| Standard | balance | ≤0.015 | ≤0.015 | ≤0.05 | ≤0.15 | ≤0.015 | ≤0.15 | 0.50-0.70 | 1.60-1.90 | 3.80-4.20 |
| Classic | - | 0.005 | 0.008 | 0.02 | 0.1 | 0.011 | 0.1 | 0.52 | 1.75 | 3.85 |
Sieve analysis (particle size distribution) | ||||||
| μm | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
| wt% | trace | ≤1 | balance | balance | balance | 10-30 |
| Classic | 0 | 0.7 | 19.7 | 25.7 | 31.8 | 22.1 |
Properties
LAP100.29D2+0.3%C+0.6%Zn-st, condition: temperature1120℃, sintering time 30min.
Package and delivery
1000kg per big flexbag and 25kg per small bag packed into one big bag
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.
LAP100.29D1: Add Ni(1.70-2.10%)and Cu(1.60-1.90%)in to the base powder(LAP100.29Mo1)mix uniformly. It enables the powder has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials.
·The powder has high compressibility and high strength.
·By adding superfine Cu powder improves powders uniformity and stability.
·Suitable for production of high strength and high dimensional precision high quality PM parts.
| Product standard and content(wt%) | ||||||||||
| Composition | Fe | C | S | Si | Mn | P | O | Mo | Cu | Ni |
| Standard | balance | ≤0.015 | ≤0.015 | ≤0.05 | ≤0.15 | ≤0.015 | ≤0.15 | 0.5-0.7 | 1.6-1.9 | 1.7-2.1 |
| Classic | - | 0.006 | 0.008 | 0.03 | 0.1 | 0.01 | 0.11 | 0.52 | 1.72 | 1.75 |
Sieve analysis (particle size distribution) | ||||||
| um | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
| wt% | trace | ≤1 | balance | balance | balance | 10-30 |
| Classic | 0 | 0.3 | 16.5 | 25 | 30.2 | 20.8 |
Properties
LAP100.29D1+0.3%C+0.6%Zn-st, condition: temperature1120℃, sintering time 30min.
LAP100.29D2: Add Ni(3.80-4.20%)and Cu(1.60-1.90%)into the base powder(LAP100.29Mo1) mix uniformly.Due to its high Ni content, it is suitable for production of high hardcnability and high strength parts.
·The powder has high compressibility and high strength.
·No segregation enables the stability of product's sintered size.
·The increase of Ni content improves the hardenability of the material.
·Suitable for the production of large parts which need heat treatment.
| Product standard and content(wt%) | ||||||||||
| Composition | Fe | C | S | Si | Mn | P | O | Mo | Cu | Ni |
| Standard | balance | ≤0.015 | ≤0.015 | ≤0.05 | ≤0.15 | ≤0.015 | ≤0.15 | 0.50-0.70 | 1.60-1.90 | 3.80-4.20 |
| Classic | - | 0.005 | 0.008 | 0.02 | 0.1 | 0.011 | 0.1 | 0.52 | 1.75 | 3.85 |
Sieve analysis (particle size distribution) | ||||||
| μm | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
| wt% | trace | ≤1 | balance | balance | balance | 10-30 |
| Classic | 0 | 0.7 | 19.7 | 25.7 | 31.8 | 22.1 |
Properties
LAP100.29D2+0.3%C+0.6%Zn-st, condition: temperature1120℃, sintering time 30min.
Package and delivery
1000kg per big flexbag and 25kg per small bag packed into one big bag
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.