Availability: | |
---|---|
LAP100.29S1 and LAP100.29S2 are prealloyed powder which contains Mn and S added by melting to make MnS clamps precipitated during solidification. MnS will play the role of lubricants when machining. The parts made of the prealloyed powder will increase tool life and save much production cost accordingly.
LAP100.29S1 | |||
Chemical Properties(%) | Unit | Specification | |
Min | Max | ||
C | % |
| 0.02 |
Si | % |
| 0.05 |
Mn | % | 0.10 | 0.30 |
P | % |
| 0.02 |
S | % | 0.30 | 0.40 |
HL | % |
| 0.25 |
Physical Properties | |||
Apparent density | g/cm3 | 2.90 | 3.10 |
Flow rate | s/50g |
| 30.00 |
Green density 490Mpa | g/cm3 | 6.70 |
|
Particle size distribution(%) | |||
180-212um | % |
| 1 |
150-180um | % |
| 10 |
45-150um | % |
|
|
-45um | % | 10 | 30 |
LAP100.29S2 | |||
Chemical Properties(%) | Unit | Specification | |
Min | Max | ||
C | % |
| 0.02 |
Si | % |
| 0.05 |
Mn | % | 0.10 | 0.30 |
P | % |
| 0.02 |
S | % | 0.20 | 0.30 |
HL | % |
| 0.25 |
Physical Properties | |||
Apparent density | g/cm3 | 2.90 | 3.10 |
Flow rate | s/50g |
| 30.00 |
Green density 490Mpa | g/cm3 | 6.70 |
|
Particle size distribution(%) | |||
180-212um | % |
| 1 |
150-180um | % |
| 10 |
45-150um | % |
|
|
-45um | % | 10 | 30 |
Application
LAP100.29S1 and LAP100.29S2 is widely used for the production of PM parts require more cutting after sintering.
LAP100.29S1 and LAP100.29S2 are prealloyed powder which contains Mn and S added by melting to make MnS clamps precipitated during solidification. MnS will play the role of lubricants when machining. The parts made of the prealloyed powder will increase tool life and save much production cost accordingly.
LAP100.29S1 | |||
Chemical Properties(%) | Unit | Specification | |
Min | Max | ||
C | % |
| 0.02 |
Si | % |
| 0.05 |
Mn | % | 0.10 | 0.30 |
P | % |
| 0.02 |
S | % | 0.30 | 0.40 |
HL | % |
| 0.25 |
Physical Properties | |||
Apparent density | g/cm3 | 2.90 | 3.10 |
Flow rate | s/50g |
| 30.00 |
Green density 490Mpa | g/cm3 | 6.70 |
|
Particle size distribution(%) | |||
180-212um | % |
| 1 |
150-180um | % |
| 10 |
45-150um | % |
|
|
-45um | % | 10 | 30 |
LAP100.29S2 | |||
Chemical Properties(%) | Unit | Specification | |
Min | Max | ||
C | % |
| 0.02 |
Si | % |
| 0.05 |
Mn | % | 0.10 | 0.30 |
P | % |
| 0.02 |
S | % | 0.20 | 0.30 |
HL | % |
| 0.25 |
Physical Properties | |||
Apparent density | g/cm3 | 2.90 | 3.10 |
Flow rate | s/50g |
| 30.00 |
Green density 490Mpa | g/cm3 | 6.70 |
|
Particle size distribution(%) | |||
180-212um | % |
| 1 |
150-180um | % |
| 10 |
45-150um | % |
|
|
-45um | % | 10 | 30 |
Application
LAP100.29S1 and LAP100.29S2 is widely used for the production of PM parts require more cutting after sintering.