LAP100.29A2: Add Cr, Ni, Mo, Co into the molten steel, which enables the all alloy elements fully integrated into the molten steel. The powder has high strength,good heat treatment performance and corrosion resistance. This type of power is mainly used for production of high strength sintered machine parts, wear resistant parts, corrosion resistant in bad working environment sintered parts,e.g.valve seats.
Advantages：
·The alloy elements distribute uniformly and without segregation, which has uniform physical and chemical sintering properties.
·This type of powder can be used to produce high strength, corrosion resistance,wear resistance and oxidation resistance sintered structural parts.
Specification
Chemical Properties（%） | Unit | Specification | |
| Min | Max | ||
| C | % | 0.01 | |
| Si | % | 0.05 | |
| Mn | % | 0.20 | 0.50 |
| P | % | 0.02 | |
| S | % | 0.015 | |
| Cr | % | 0.10 | 0.30 |
| Ni | % | 0.50 | 0.90 |
| Mo | % | 0.35 | 0.65 |
| Co | % | 0.30 | 0.50 |
| Cu | % | 0.50 | |
| H2-Loss | % | 0.25 | |
| Physical Properties | |||
| Apparent density | g/cm3 | 2.90 | 3.15 |
| Flow rate | s/50g | 28 | |
| Green density 600Mpa | g/cm3 | 6.85 | |
| Particle size distribution（%） | |||
| 180-212um | % | 1 | |
| 150-180um | % | 10 | |
| 45-150um | % | ||
| -45um | % | 10 | 30 |
Properties
LAP100.29A2+0.5%C+0.8%Zn-st, condition: temperature 1125℃, sintering time 30min.
Specifications of other Ni-Mo Alloy Powders
Product Packing
25kg/bag, 1000kg/bag, the package can be customized by buyer's requirements.
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.
LAP100.29A2: Add Cr, Ni, Mo, Co into the molten steel, which enables the all alloy elements fully integrated into the molten steel. The powder has high strength,good heat treatment performance and corrosion resistance. This type of power is mainly used for production of high strength sintered machine parts, wear resistant parts, corrosion resistant in bad working environment sintered parts,e.g.valve seats.
Advantages：
·The alloy elements distribute uniformly and without segregation, which has uniform physical and chemical sintering properties.
·This type of powder can be used to produce high strength, corrosion resistance,wear resistance and oxidation resistance sintered structural parts.
Specification
Chemical Properties（%） | Unit | Specification | |
| Min | Max | ||
| C | % | 0.01 | |
| Si | % | 0.05 | |
| Mn | % | 0.20 | 0.50 |
| P | % | 0.02 | |
| S | % | 0.015 | |
| Cr | % | 0.10 | 0.30 |
| Ni | % | 0.50 | 0.90 |
| Mo | % | 0.35 | 0.65 |
| Co | % | 0.30 | 0.50 |
| Cu | % | 0.50 | |
| H2-Loss | % | 0.25 | |
| Physical Properties | |||
| Apparent density | g/cm3 | 2.90 | 3.15 |
| Flow rate | s/50g | 28 | |
| Green density 600Mpa | g/cm3 | 6.85 | |
| Particle size distribution（%） | |||
| 180-212um | % | 1 | |
| 150-180um | % | 10 | |
| 45-150um | % | ||
| -45um | % | 10 | 30 |
Properties
LAP100.29A2+0.5%C+0.8%Zn-st, condition: temperature 1125℃, sintering time 30min.
Specifications of other Ni-Mo Alloy Powders
Product Packing
25kg/bag, 1000kg/bag, the package can be customized by buyer's requirements.
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts.