LAP100.29 is a kind of ultra-pure water atomized iron powder. With apparent density 2.95-3.10g/cm3, good compressive performance, wide range of application, and it is widely used in the production of high strength and high density sintered structural parts.
·High purity, easy to compress, good formability, used in the production of high density PM parts.
·Can be used for production of iron magnetic material matrix.
·Used for production of high strength sintered structural parts, which can be used for subsequent processing of heat treatment.
Product standard and content(wt%) | |||||||
Composition | Fe | C | S | Si | Mn | P | O |
Standard | ≥99.2 | ≤0.01 | ≤0.015 | ≤0.04 | ≤0.14 | ≤0.015 | ≤0.20 |
Classic | 99.57 | 0.004 | 0.009 | 0.03 | 0.1 | 0.01 | 0.11 |
Sieve analysis (particle size distribution) | ||||||
um | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
wt% | 0 | <10 | balance | balance | balance | 15-30 |
Classic | 0 | 2.5 | 21.2 | 25.6 | 29.3 | 21.4 |
Properties
Composition: Fe-1.5%; Cu-0.6%; Gr-0.8ZnSt. Sintering condition: 1120℃ × 30 min, cracked ammonia.
Package and delivery
1000kg per big flexbag and 25kg per small bag packed into one big bag.
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts. LAP100.29 is widely used for the production of sintered metal parts with density above 6.8 g/m³and PM forged parts.
LAP100.29 is a kind of ultra-pure water atomized iron powder. With apparent density 2.95-3.10g/cm3, good compressive performance, wide range of application, and it is widely used in the production of high strength and high density sintered structural parts.
·High purity, easy to compress, good formability, used in the production of high density PM parts.
·Can be used for production of iron magnetic material matrix.
·Used for production of high strength sintered structural parts, which can be used for subsequent processing of heat treatment.
Product standard and content(wt%) | |||||||
Composition | Fe | C | S | Si | Mn | P | O |
Standard | ≥99.2 | ≤0.01 | ≤0.015 | ≤0.04 | ≤0.14 | ≤0.015 | ≤0.20 |
Classic | 99.57 | 0.004 | 0.009 | 0.03 | 0.1 | 0.01 | 0.11 |
Sieve analysis (particle size distribution) | ||||||
um | 180 | 180/150 | 150/106 | 106/75 | 75/45 | -45 |
wt% | 0 | <10 | balance | balance | balance | 15-30 |
Classic | 0 | 2.5 | 21.2 | 25.6 | 29.3 | 21.4 |
Properties
Composition: Fe-1.5%; Cu-0.6%; Gr-0.8ZnSt. Sintering condition: 1120℃ × 30 min, cracked ammonia.
Package and delivery
1000kg per big flexbag and 25kg per small bag packed into one big bag.
Application
This type of metal powder can be used for the material of powder metallurgy sinter component parts. LAP100.29 is widely used for the production of sintered metal parts with density above 6.8 g/m³and PM forged parts.